Electropolishing, also known as electrochemical polishing, anodic polishing or electrolytic polishing (especially in the metallography field), is an electrochemical process that removes material from a metallic workpiece. It is used to polish, passivate, and deburr metal parts. It is often described as the reverse of electroplating. It may be used in lieu of abrasive fine polishing in microstructural preparation.
Maps, Directions, and Place Reviews
Mechanism
Typically, the work-piece is immersed in a temperature-controlled bath of electrolyte and serves as the anode; it is connected to the positive terminal of a DC power supply, the negative terminal being attached to the cathode. A current passes from the anode, where metal on the surface is oxidised and dissolved in the electrolyte, to the cathode. At the cathode, a reduction reaction occurs, which normally produces hydrogen. Electrolytes used for electropolishing are most often concentrated acid solutions having a high viscosity, such as mixtures of sulphuric acid and phosphoric acid. Other electropolishing electrolytes reported in the literature include mixtures of perchlorates with acetic anhydride and methanolic solutions of sulphuric acid.
To achieve electropolishing of a rough surface, the protruding parts of a surface profile must dissolve faster than the recesses. This process, referred to as anodic levelling, can be subject to incorrect analysis when measuring the surface topography. Anodic dissolution under electropolishing conditions deburrs metal objects due to increased current density on corners and burrs. Most importantly, successful electropolishing should operate under diffusion limited constant current plateau, achieved by following current dependence on voltage (polarisation curve), under constant temperature and stirring conditions.
Stainless Steel Cleaner Diy Video
Applications
Electropolishing has many applications in the metal finishing industry because of its simplicity and its ability to be used on irregularly-shaped objects, such as electropolished stainless steel drums of washing machines, stainless steel surgical devices, and copper semiconductors. Electropolishing is also commonly used to prepare thin metal samples for transmission electron microscopy because the process does not cause the mechanical deformation of surface layers observed with mechanical polishing. Ultra high vacuum (UHV) components are typically electropolished in order to have a smoother surface for improved vacuum pressures, out-gassing rates, and pumping speed.
Standards
- ISO.15730:2000 Metallic and other Inorganic Coatings - Electropolishing as a Means of Smoothing and Passivating Stainless Steel
- ASME BPE Standards for Electropolishing Bioprocessing Equipment
- SEMI F19, Electropolishing Specifications for Semiconductor Applications
- ASTM B 912-02 (2008), Passivation of Stainless Steels Using Electropolishing
- ASTM E1558, Standard Guide for Electrolytic Polishing of Metallographic Specimens
Benefits of electropolishing (stainless steel)
One of the benefits of electropolishing for stainless steel is that it removes iron from the surface and enhances the chromium/nickel content for the most superior form of passivation for stainless steel. Electropolishing also provides a clean and smooth surface that is easier to sterilise, while improving the surface finish by levelling micro-peaks and valleys. This methodology is able to polish areas that are inaccessible by other polishing methods.
Another benefit of electropolishing is that it removes a small amount of material (typically 20-40 micrometre in depth in the case of stainless steel) from the surface of the parts, while also removing small burrs or high spots. It can be used to reduce the size of some parts when necessary. The results of electropolishing are considered to be aesthetically pleasing by many people.